ASTM G38 PDF

ASTM G Standard Practice for Making and Using C-Ring Stress-Corrosion Test Specimens. ASTM G(). Standard Practice for Making and Using C-Ring Stress- Corrosion Test Specimens. standard by ASTM International. Find the most up-to-date version of ASTM G38 at Engineering

Author: Dukinos Zuluk
Country: Netherlands
Language: English (Spanish)
Genre: Science
Published (Last): 4 December 2015
Pages: 391
PDF File Size: 5.40 Mb
ePub File Size: 18.52 Mb
ISBN: 277-3-43597-199-8
Downloads: 5545
Price: Free* [*Free Regsitration Required]
Uploader: Samuran

Due to the very large number of tests offered, descriptions of those most commonly requested have been gathered into the following groups:.

In this case, however, the alloy was reported to be resistant to SCC in the NaCl brine service environment. Touchstone Research Laboratory, Ltd.

Stress Corrosion Cracking of Stainless Steel. In many cases, SCC involves the combination of tensile stress and local anodic attack which dictate the period of incubation prior to the initiation of SCC. Touchstone Engineers have experience with Stress-Corrosion Testing and are able to accurately determine when the specimen fractured and obtain a precise cracking time.

ASTM G38 – Standard Practice for Making and Using C-Ring Stress-Corrosion Test Specimens

This practice covers the features of design and machining, and procedures for stressing, exposing, and inspecting C-ring type of stress-corrosion test specimens. Please email info trl.

Therefore, to conduct tests for SCC, either mechanical or electrochemical means are often utilized to promote localized corrosion so that the inherent susceptibility of the material can be determined. Stress of principal interest in the C-ring specimen is the circumferential stress because this stress is not uniform.

  INTERNATIONAL GTA220 PDF

Stress Corrosion Cracking of Stainless Steel – The example shown indicates many intersecting, branched cracks with a transgranular propagation mode. An analysis is given of the state and distribution of stresses in the C-ring.

Under the sleeve, evidence of severe general and pitting corrosion were found and evidence of sulfur-containing corrosion products. Touchstone takes care that the specimens are supported by nothing more than the corrosive medium comes into contacted with the critically stressed area of the specimen.

The example shown indicates many intersecting, branched cracks with a transgranular propagation mode. In some cases, where constant load tests are used, environmental cracks can initiate but not propagate through the entire cross-section of the specimen. The location of cracking was limited to a region covered by an elastomeric sleeve.

ASTM F titanium aircraft engine cleaning materials.

Therefore, the specimen may not fail, but significant cracking may take place. SCC is the brittle cracking of a metal due to the result of combined effects from localized corrosion and tensile stress. This local environment resulted in enhanced localized susceptibility of the material to pitting corrosion and SCC. Care must be taken during machining so that specimens are not overheated, are not g83 deformed and do not develop residual stresses in the metal surface.

ASTM G – practice for preparation g8 use of bent-beam scc test specimens. ASTM G – practice for evaluation of scc resistance of metals and alloys in 3.

Determination of the cracking time may be subjective due g8 the visual examination. Stress Corrosion Cracking Stress Corrosion Testing Description SCC is the brittle cracking of a metal due to the result of combined effects from localized corrosion and tensile stress. Analysis of the elastomer indicate that it was not the correct grade and chemical degradation had occurred in service to produce organic acids and sulfur compounds.

  KARABINY AVALONU PDF

ASTM G38 – 01 Standard Practice for Making and Using C-Ring Stress-Corrosion Test Specimens

ASTM D steels caustic. ASTM G – practice for preparation of scc test specimens for weldments. Select from list below: Prevention or Remedial Action. These are typical of stress corrosion cracking SCC in austenitic stainless steel. Prevention or Remedial Action lower either g8 or residual tensile stresses.

When the specimen is stressed by measuring the strain on the tension surface of the c-ring, the strain gage should be positioned in the middle of the arc in order to indicate the maximum strain. To request a quotation for any test email info trl. There are also transverse stresses present; however, these stresses may decrease with decreasing width to thickness and increasing diameter to thickness ratios.

Such techniques include the use of slow strain rate, cyclic slow strain rate, fracture mechanics and electrochemical potential control. Due to the very large number of tests offered, descriptions of those most commonly g388 have been gathered into the following groups: ASTM G – practice for preparation and use of direct tension scc test specimens.